Type: | Ionite Membrane |
---|---|
Membrane Type: | Other |
Material: | Resin |
Technology: | Extrusion |
Thickness: | 125 |
Weight: | 246 |
Customization: |
---|
Suppliers with verified business licenses
Membrane Type | Thickness(microns)(um) | Weight(g/m2) |
T-N-115 | 125 | 246 |
T-N-117 | 62 | 122 |
T-N-1110 | 75 | 148 |
T-N-115W/T-N-116W/T-N-117W | 80 | 172 |
Physical and OtherProperties | Index Parameters | Test Method | |
Tensile Test (23°C, 50% RH) | T-N-11 X | T-N-11X W | - |
Tensile Strength(MPa) | ≥28 | GB/T20042.3-2022 | |
Tensile Modulu(MPa) | ≥400 | GB/T20042.3-2022 | |
Elongation at break(%) | ≥120 | GB/T20042.3-2022 | |
Specific Gravity | 1.97 | - | |
Other Properties | Index Parameters | Test Method | |
2 Conductivity(S/cm) | ≥0.100 | ≥0.100 | GB/T20042.3-2022 |
3 Acid Capacity(meq/g) | 1.00±0.05 | 1.00±0.05 | GB/T20042.3-2022 |
Dissolved Hydrogen Concentration(ppb) | 1000 |
Hydrolytic Properties | Index Parameters T-N-11X |
Index Parameters T-N-11XW |
Test Method |
5 Water Content(%) | 5.0±3.0 | 5.0±3.0 | GB/T 20042.3-2022 |
6 Water Uptake(%) | 50.0±5.0 | 50.0±5.0 | GB/T 20042.3-2022 |
(23ºC, 50% RH)Thickness Change,% increase | |||
from50% RH, 23ºCtowatersoaked,23ºC | ≤ 5 | ≤ 18 | |
From 50% RH,23ºCtowatersoaked 100ºC | ≤ 15 | ≤ 30 | |
from50% RH, 23ºCtowatersoaked,23ºC | ≤ 5 | ≤ 16 | GB/T 20042.3-2022 |
From 50% RH,23ºCtowatersoaked 100ºC | ≤ 18 | ≤ 20 | GB/T 20042.3-2022 |