N-117 Proton Exchange Membrane for Electrolyzer Membrane Electrolytic of Water

• Type: Ionite Membrane
• Membrane Type: Pem
• Thickness: 125-220um
• Weight: 246-432 G/M2
• Transport Package: Carton Packing
• Specification: 1 Square meter
• Model NO.: T-N-117
• Trademark: Thinkru
• Origin: China
• HS Code: 3921909001
• Production Capacity: 50000

Product Description

Pronton exchange membrane for PEMWE
According to specific application scenarios,Thinkru proton 
exchange membrane for hydrogen production from electrolytic watercan be divided into 11x series proton exchange membrane for industrial hydrogen production and 1lxW   series proton exchange 
membrane for hydrogen health.Nepem proton exchange membrane 
for electrolytic water has the characteristics of high conductvity, low gas permeabllity and high pressure resistance.

 

Special membrane for electrolyzed water: T-N-115
Special film for hydrogen absorption machine and hydrogen-rich water cup: T-N-115W
The difference between T-N-115/T-N115W is that T-115W has no odor, and the processing formula is different.


T-N-11x Series(T-N-115/T-N-117):
The T-N-11x series membrane is a perfluorinated sulfonate resin homogeneous membrane, that has excellent heat resistance, mechanical properties, electrochemical properties Chemical properties and chemical stability, can be used in strong acid, strong alkali, strong oxidation, and other harsh conditions, and is widely used in industrial PEM electrolytic hydrogen production and other fields.


T-N-11X W Serie (T-N-115W/T-N-116W/T-N-117W):
Compared with T-N-11X series membranes, W-series membranes optimize the formulation and treatment process of membrane preparation liquid and have lower solvent residue, which is widely used in the field of hydrogen health.

1.Thickness and Basis Weight Properties

Membrane Type	Thickness(microns)(um)	Weight(g/m2)
T-N-115	125	246
T-N-117	62	122
T-N-1110	75	148
T-N-115W/T-N-116W/T-N-117W	80	172

2.PhysicalandOtherProperties

Physical and OtherProperties	Index Parameters		Test Method
Tensile Test (23°C, 50% RH)	T-N-11 X	T-N-11X W	-
Tensile Strength(MPa)	≥28		GB/T20042.3-2022
Tensile Modulu(MPa)	≥400		GB/T20042.3-2022
Elongation at break(%)	≥120		GB/T20042.3-2022
Specific Gravity	1.97		-
Other Properties	Index Parameters		Test Method
2 Conductivity(S/cm)	≥0.100	≥0.100	GB/T20042.3-2022
3 Acid Capacity(meq/g)	1.00±0.05	1.00±0.05	GB/T20042.3-2022
Dissolved Hydrogen Concentration(ppb)		1000

 

 

3.Hydrolytic Properties

 

Hydrolytic Properties	Index Parameters T-N-11X	Index Parameters T-N-11XW	Test Method
5 Water Content(%)	5.0±3.0	5.0±3.0	GB/T 20042.3-2022
6 Water Uptake(%)	50.0±5.0	50.0±5.0	GB/T 20042.3-2022
(23ºC, 50% RH)Thickness Change,% increase
from50% RH, 23ºCtowatersoaked,23ºC	≤ 5	≤ 18
From 50% RH,23ºCtowatersoaked 100ºC	≤ 15	≤ 30
from50% RH, 23ºCtowatersoaked,23ºC	≤ 5	≤ 16	GB/T 20042.3-2022
From 50% RH,23ºCtowatersoaked 100ºC	≤ 18	≤ 20	GB/T 20042.3-2022

1.Measurements taken with membrane conditioned to23°C,50%RH.

2.Conductivity measurements a23°C,100%RH.

3.A base titration procedure measures the equivalents of sulfonic acid group in the polymer resin,and uses the measurementto calculate 
the acid capacity orequivalent weight ofthe membrane.

4.Dissolved hydrogen concentration was performed using a hydrogen-rich watertest pen (ENH-1000 Portable Dissolved hydrogen Meter), 
which was based on the principle of oxidation reduction potential in the solution to calculate the dissolved hydrogen concentration.

5.Watercontent of membrane conditioned to 23ºC and 50% RH (dryweight basis).
6.Wateruptake from dry membrane to conditioned in water at 100ºCfor1 hour (dryweight basis).