Composite Ion Exchange Membrane for Electrolysis or Electroplating Pem for Test

• Customization: Available
• Membrane Type: Plate and frame
• Type: Ionite membrane
• Model NO.: T-N-417
• Thickness: 260um
• Specific Gravity: 1.35
• Tensile Strength: 40MPa
• Transport Package: Multi-Layer Packaging
• Specification: Customized
• Trademark: Thinkru
• Origin: China
• HS Code: 8421292000
• Production Capacity: 50000

Product Description

Cosposite PEM,formed by using unique tape casting process with appropriate molecular weight and ion exchange capacity of perfluorosulfonic acid resin,and uniform thickness, is widely used in electrolytic chlorine dioxide generator, etching solution recovery copper, gold salt preparation, amino acid refining, caustic soda preparation, electrodialysis and other electrolytic industries.

 

1. Thickness and Basis Weight Properties

MembraneType	Thickness(microns)	Weight(g/m 2)
T-N-417	260	340
T-N-4110	360	470

2. Physical and Other Properties

Physical and Other Properties	Index Parameters	Test Method
TensileTest(23°C,50%RH)
Tensile Strength(MPa)	≥40	GB/T 20042.3-2022
Elongation at break(%)	≥100	GB/T 20042.3-2022
Specific Gravity	1.35	-
Other Properties
Conductivity 2(S/cm)	≥0.100	GB/T 20042.3-2022
Acid Capacity 3(meq/g	1.00±0.05	GB/T 20042.3-2022

3. Hydrolytic Properties

Hydrolytic Properties	Index Parameters	Test Method
Water Content 4(%)	5.0±3.0	GB/T 20042.3-2022
Water Uptake 5(%)	50.0±5.0	GB/T 20042.3-2022
from 50% RH,23°C to water soaked,23°C	≤5	GB/T 20042.3-2022
from 50% RH,23°C to water soaked,100°C	≤10	GB/T 20042.3-2022
Linear expansion,%increase
from 50% RH,23°C to water soaked,23°C	≤2	GB/T 20042.3-2022
from 50% RH,23°C to water soaked,100°C	≤5	GB/T 20042.3-2022

1, Measurements taken with membrane conditioned to 23°C,50%RH.

2, Conductivity measurements at 23°C,100%RH.

3, A base titration procedure measures the equivalents of sulfonic acid in the polymer,  and uses the measurement to calculate the acid capacity or equivalent weight of the pure polymer.

4, Water content of membrane conditioned to 23°C and 50% RH(dry weight basis).

5, Water uptake from dry membrane to conditioned in water at 100°C for 1 hour (dry weight basis).